In the present work, a comparative study of the shape memory and thermomechanical behavior of four alloys containing different amount of samarium have been carried out at a strain rate of 0.08x10 -6 s -1 . After hot rolling, annealing and solution treatment, the alloy samples were tensile deformed at room temperature from 1% to 5% and were then recovered at 600̊C for 20 minutes repeatedly for six times to complete six training cycles. It has been found that the addition of samarium strengthens the austenitic matrix, increases the c/a ratio and reduces the grain size. It has been noticed that the addition of samarium (0.64 wt. %) improves the shape memory effect when the alloys were strained from 1% to 5%. This improvement in shape memory effect presumably can be regarded as the increase in strength, increase in c/a ratio and absence of ά (martensite). It has been further noticed that when samarium contents are gradually reduced from 0.64 % to 0.21% the shape memory effect decreases. The decrease in shape memory effect by the decrease in samarium contents can be attributed to decrease in strength, decrease in c/a ratio and formation of ά (martensite). It has been further noticed that the shape memory effect decreases with the increase in amount of strain. It is found that thermomechanical treatment (training) results in improvement of shape memory effect and has a significant influence on mechanical parameters like proof stress (σ 0.002 ), critical stress (σ 0.0008 ) and strain hardening exponent. The improvement in shape memory effect by thermomechanical treatment can be regarded as the effect of reduction in the values of proof stress and critical stress during training which facilitates the formation of ε (martensite). It has also been noticed that excessive training may result in the formation of ά (martensite) due to continuous softening of the alloy during training, thus degrading the shape memory effect. Finally, it has also been noticed that the addition of samarium increases the values of proof stress, critical stress and strain hardening exponent. Although the addition of samarium increases the values of proof stress, critical stress and strain hardening exponent yet it has not an adverse effect on shape memory effect.
Subject/Specialization
Language
Program
Faculty/Department's Name
Institute Name
Univeristy Type
Public
Private
Campus (if any)
Institute Affiliation Inforamtion (if any)
City where institute is located
Province
Country
Degree Starting Year
Degree Completion Year
Year of Viva Voce Exam
Thesis Completion Year
Thesis Status
Completed
Incomplete
Number of Pages
Urdu Keywords
English Keywords
Link
Select Category
Religious Studies
Social Sciences & Humanities
Science
Technology
Any other inforamtion you want to share such as Table of Contents, Conclusion.
Your email address*